Overview
LDPE fim grade has excellent physical properties, good processability, high mechanical strength and good stainability, printability and sealability. The resin is resistant to moisture, oil and chemical corrosion and has excellent high-speed processing properties.
Applications
LDPE film grade can be used for heat shrinkable packaging film,
laminated film, freezing film, medical packaging, multi-ayer co-
extrusion film, heavy-duty packaging film, pipe coatings, cable
sheathing, lining and high-end chemical foaming.
Grades and Typical Values (Not Warranted Values)
| Grades | 2100TN00 | N210 | S030 | N220 | |
| MFR | g/10min | 0.30 | 2.1 | 0.3 | 2.2 |
| Density | 23℃,g/cm³ | 0.920 | 0.921 | 0.920 | 0.922 |
| Haze | % | 14 | 16 | 16 | 16 |
| Tensile Strength | MPa | 14 | 11 | 15 | |
| Elongation at break | % | 550 | 550 | 500 | |
| Certifications | FDA | ROHS/FDA | ROHS/FDA | ||
| Grades | N150 | LD165 | 2420D | 2426H | |
| MFR | g/10min | 1.5 | 0.33 | 0.35 | 2 |
| Density | 23℃,g/cm³ | 0.919 | 0.922 | 0.924 | 0.924 |
| Haze | % | 24 | 1 | ||
| Tensile Strength | MPa | 12.5 | ≥200 | 15 | 12 |
| Elongation at break | % | 550 | 500 | 580 | |
| Certifications | ROHS/FDA | GB/T19001-2016/ISO9001
GB/T24001-2016 GB/T45001-2020 |
|||
| Grades | Q210 | Q281 | Q400 | 951-000 | |
| MFR | g/10min | 2.1 | 2.8 | 4.0 | 2.17 |
| Density | 23℃,g/cm³ | 0.921 | 0.924 | 0.923 | 0.92 |
| Haze | % | 10 | 10 | 10 | 9 |
| Tensile Strength | MPa | 11 | 11 | 16 | 8 |
| Elongation at break | % | 550 | 550 | 450 | 400 |
| Certifications | ROHS/FDA | ROHS/FDA | ROHS/FDA | ROHS/FDA | |
| Grades | 951-050 | 2426K | 2426H | 2520D | 951-050 | |
| MFR | g/10min | 2.17 | 4.0 | 1.9 | 0.3 | 2.8 |
| Density | 23℃,g/cm³ | 0.92 | 0.926 | 0.923 | 0.924 | 0.925 |
| Haze | % | 9 | 10 | 8 | 11 | 7.7 |
| Tensile Strength | MPa | 8 | 18 | 15 | 11 | 11.3 |
| Elongation at break | % | 400 | 550 | 600 | 600 | 620 |
| Applications | Medical packaging film | |||||
| Certifications | ROHS/FDA/PAHS | ROHS/ FDA/ PAHS | ROHS/ FDA/ PAHS | ROHS/ FDA | ||
| Grades | LD100AC | LD100-PC | 2102TN00 | 2102TN26 | |
| MFR | g/10min | 2 | 2 | 2.40 | 2.40 |
| Density | 23℃,g/cm³ | 0.9225 | 0.9225 | 0.920 | 0.920 |
| Haze | % | ≤9 | 7 | ||
| Tensile Strength | MPa | 9 | 11 | 12 | 11 |
| Elongation at break | % | 500 | 550 | 450 | |
|
Certifications |
FDA |
GB/T19001-2016/ISO9001
GB/T24001-2016 GB/T45001-2020 |
FDA |
FDA |
|
| Grades | QLT04 | QLF39 | |
| MFR | g/10min | 3.0 | 0.75 |
| Density | 23℃,g/cm³ | 0.920 | 0.920 |
| Haze | % | 10 | |
| Tensile Strength | MPa | 6 | 6 |
| Elongation at break | % | 550 | 550 |
| Certifications | FDA | FDA | |
Package, Storage and Transportation
The resin is packaged in internally film-coated polypropylene woven bags, brown paper bags or laminated polyethylene film bags. The net weight is 25Kg/bag.
The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air. During transportation, the material should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.